Spring Steel Sheets And Plates

Product Details:

IS 4454 Spring Steel wire is a top quality product which is suitable for making springs for various applications. Our product suite features spring steel wires in phosphatized and reddish/dry-bright finish in various ring formats. The 3 different grades of spring steel wire that are manufactured by us are: Grade I: Should be used for springs and wire form subjected to static load or low load cycles low stressed. Grade II: Should be used for springs and wire form subjected to moderate load cycles - moderately stressed. Grade III: Should be used for highly stressed springs, for springs under moderate to high dynamic stresses and in smaller diameters even for impact loaded springs.

 

Application:

• It finds application in varied types of industries ranging from automotive to mattress springs, and for various end uses like spring, spring washer, chain bush, tiller spring, etc.

 

Standards:

• IS: 4454 (Part I)

Product Details:

EN47 Spring SteelPDF datasheet

EN47 spring steel stockholders and suppliers, delivering to the whole of the UK. West Yorkshire Steel are suppliers of EN47 chromium vanadium type spring steel supplied in the as rolled condition. EN47 is suitable for oil hardening and tempering. When used in the oil hardened and tempered condition EN47 spring steel combines spring characteristics with good wear and abrasion resistance. When hardened EN47 offers excellent toughness and shock resistance which make it a suitable alloy spring steel for parts exposed to stress, shock and vibration.


We welcome export enquiries for spring steel. Contact our sales office and consult our shipping policy for further details.

 

Related Specifications:

• BS970 735A50 735A51 1.8159 AISI 6150 50CrV4 50CV4 ASTM A829

Suppliers of round bar we can offer diameters in EN47 sawn to your required lengths as 1 offs or multiple cut pieces. Ground steel bar can be supplied, providing a high quality precision ground spring steel bar to tight tolerances.       

Applications:

• EN47 is used widely in the motor vehicle industry and many general engineering applications. Suitable for applications that require high tensile strength and toughness. Typical applications include crankshafts, steering knuckles, gears, spindles and pumps.

Forging:  

• Preheat the steel carefully, then raise temperature to 1050°C for forging. Do not forge below 840°C. After forging EN47 spring steel cool slowly, preferably in a furnace.

Annealing:  

• Heat slowly to 820-840°C, soak well. Cool slowly in the furnace.

Hardening:   

• Heat slowly to 650-700°C and thoroughly soak. Continue to heat the steel to the final hardening temperature of 830-860°C and allow the component to be heated through. Quench in oil.

Tempering   

• Temper the EN47 spring steel component immediately after quenching whilst tools are still hand warm. Re-heat to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. For most applications tempering of this grade will be between 400-600°C.

Heat Treatment   

• Heat treatment temperatures, including rate of heating, cooling and soaking times etc. will vary due to factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of EN47.

Product Details:

Material specification sheet Saarstahl - 51CrV4 (50CrV4)Material No.1.8159Former brand name:F 2 K International steel grades:BS: 735A51, 735M50, 735H51AFNOR: 50CrV4, 51CV4SAE: 6150Material group: Steel for quenching and tempering according to DIN EN 10083Chemical C Si Mn Cr V other composition:(Typical analysis in %) 0,50 0,25 0,90 1,10 0,12 (Pb)Application: Alloyed heat treatable steel with a typical tensile strength of 900 - 1200N/mm². For automotive and mechanical engineering components as gear parts, pinions, shafts.Hot forming and heat treatment:Forging or hot rolling:Normalising:Soft annealing:Hardening:Tempering:1050 - 850°C 870 - 900°C/air 680 - 720°C/furnace 820 - 860°C/oil 540 - 680°C/air Treated for cold shear ability +S:Soft annealed +A:See condition Amax. 248 HB Mechanical Properties:Quenched and tempered, +QT:Diameter d [mm] < 16 >16 – 40 >40 – 100 >100 – 160 >160 – 250Thickness t [mm] < 8 850CrV4 Normativa di riferimento UNI 3545 Reference Standard UNI 3545 94 60 55 50 45 40 35 30 25 20 15 1,5 3 5 7 9 11 13 15 20 25 30 35 40 45 50 SIAU DIN W.N. AFNOR BS AISI/SAE KVR 50CrV4 1.8159 50Cr4 (6150) C Mn Si Cr 0.47 ÷ 0.55 0.70 ÷ 1.10 0.15 ÷ 0.40 0.80 ÷ 1.20 Ni - Re min. N/mm2 Rm N/mm2 A min. % KCU min. J 1330÷1580 6 - ≤ 250 - ≤ 240 10 1140 HRC / % Martensite 95% 80% 60 52 38 - mm. HRc min HRc max 1,5 3 5 7 9 11 13 15 20 25 30 35 40 45 50 57 56 56 54 52 51 50 47 42 39 37 36 35 34 33 65 65 64 64 63 63 62 61 60 58 57 55 54 53 53

Product Details:

The following material can be ordered for delivery. Contact our materials department for pricing and delivery times. For chemical analysis and other data, see pages 210–211. Please ask for information on tolerances. Spring material is supplied from our unit in Sweden and cannot be delivered in conjunction with other standard products. STRIP STEEL SS 1770, DIN 1.1231, W.NR CK 67 CK 67 is a standard quality in spring strip steel, with no corrosion resistance requirements. Available both as unhardened and hardened.

Operating temperature: -40 – +120 °C Tempering instruction: Heat to 800–820 °C, cool in oil. Temper for approx. 30 min at 400 °C, cool in air. STRIP STEEL SS 2230, EN 10089 51CrV4, W.NR 1.8159 High strength spring steel for high pressures and temperatures with a good relaxation limit. We keep a stock of the unhardened steel, which requires tempering after shaping.

Operating temperature: -40 – +225 °C SPRING STEEL SS 2331-06, EN 10270-3-1.4310, DIN 17224: X12 CrNi 17 7 Hard drawn stainless wire with good spring qualities for general use and suitable for bending. Should be tempered in 250–350 °C after shaping.

Operating temperature: -150 – +250 °C SPRING STEEL SS 2347, EN 10270-3-1.4401, DIN 17224: X5 CrNiMo 18 10 Hard drawn acid proof wire and hard rolled strip suited for naval applications, provisions, medicine and other environments where higher demands for corrosion resistance are required. Slightly lower tensile strength than stainless SS2331. Good for bending. Should be tempered in 250–350 °C after shaping.

Operating temperature: -200 – +300 °C SPRING STEEL SS 2388, EN 10270-3-1.4568, DIN 17224: X7 CrNiAl 17 7 Stainless hard rolled strip, which after tempering increases in tensile strength by approx. 350 N/mm2. This facilitates shaping as it can be performed on a softer material. The steel has excellent spring qualities with enhanced strength and a lower relaxation, even at higher temperatures.

Operating temperature: -200 – +350 °C TIN BRONZE SS 5428-7, DIN 17670/17677: SuSn6 Tin bronze (phosphor bronze) is a non-magnetic corrosion resistant spring material for low loads.

Operating temperature: -200 – +80 °C BERYLLIUM COPPER CuBe 250, DIN 17670/17677: CuBe2 Beryllium copper is a non-magnetic acid proof spring material with excellent spring qualities. This medium-hard material is easily formed, after tempering optimum spring hardness is achieved. The gas emitted during heat treatment is toxic, therefore it is important to provide good ventilation.

Operating temperature: -200 – +150 °C SPRING WIRE STATO 70, EN 10270-2-FDSiCr, DIN 17223-2: FDSiCr Stato 70 is high strength oil hardened valve spring steel. A high class spring steel for highly stressed springs. Bending is possible down to a radius equal to the wire thickness. After shaping, tempering should be done at 300–400°C. Handle carefully when supplied in ring as the wire may straighten when released. Operating

Product Details:

High carbon steels contain from 0.7 to 1.00% C with manganese ranging from 0.5% to 0.9% This steels are commonly known as spring steel. These steels are generally operated at very high stresses and heat-treated to obtain the maximum elastic limits and fatigue resistance without becoming sufficiently brittle to cause sudden failure in service. Hardenability of spring steel is very important because only fully hardened springs have the maximum resistance to take a permanent set (sagging)

We offer the following grades in spring steel:
C60, C65, C70, C75, C85, HC-14, En 42 J, C-98, C-100, C-124 / HC21 etc.

 

 

Physical Properties:
Hardness: 220HV max
Yield Strees: 290N/mm² min
Tensile Strength: 640N/mm² max

Range:
Thickness: 0.07 mm to 4.00 mm
Width: 8 mm to 500 mm (in thickness lower than 0.6 mm, 4 mm wide material can be supplied)
Hardness: Fully annealed material with a maximum hardness of 200 VPN & special temper material with hardness ranging from 230 VPN to 270 VPN.

Nextgen Steel & Alloys is a huge exporter of C80 Spring Steel in countries like Kuwait, Bahrain, Iraq, Oman, Qatar, Saudi Arabia and the United Arab Emirates (UAE), US, Singapore, Malaysia, Dubai, etc.

Additional Information:

• Item Code: C80
• Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other

Product Details:

Hardened & Tempered Steel Strips

ZENHARD, Walzen make Hardened & Tempered Medium & High Carbon Steel Strips, finds wide applications in special industrial uses. ZENHARD has excellent spring properties, uniform hardness and texture, ZENHARD has precision blanking ability and rationalizes further processing by eliminating post heat treatment & distortion and thereby increases productivity.

Walzen Strips Pvt. Ltd. manufactures ZENHARD, Hardened & Tempered Steel Strips, conforming to National and International Standards viz, IS: 2507, DIN 17222. BS: 1449, ASTM A-682 Medium & High Carbon and Low Alloy steel strips, cold rolled in-house, are heat-treated in continuous line to develop high hardness, toughness, tensile and spring properties.
Steps involved for manufacture of Hardened & Tempered Steel strips:

Hardening & Tempering:
Austenitizing of Medium & High Carbon and Low Alloy steels is carried out in 12 M long gas fired furnace with automatic controls and heat resistant S.S. Muffle to provide inert cover to the strips. Quenchingl in oil produces very hard martensite, which is then tempered down in a 7 M long electrically heated tempering furnace. Variable speed DC drive with UPS back-up ensures uninterrupted processing even during power failure.

Edge Rounding:
Rounding of one or both edges is essential for certain applications requiring high fatigue life. This is done by machining of edges with profiled carbide tips.

Grinding:
During hardening and tempering the strip surface gets oxidized, developing a Blue-grey finish. But in many application the strips are required in Bright finish. This is obtained by grinding the surfaces with waterproof-coated abrasive belts in a grinding machine with coolant flow.
ZENHARD : Chemical composition & Sizes:


Special features:

• Minimum decarburisation
• Uniform Hardness and Texture
• High degree of toughness
• Excellent Spring Properties
• Precision blanking ability
• Minimum edge camber
• Flatness across width
• No curling

Additional Information:

• Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A
• Port of Dispatch: Mumbai

Product Details:

Material specification sheet Saarstahl- C67S Material No.: 1.1231 German standard: DIN EN 10132 International steel grades: SAE:1070 JIS: S70CM Material group: Hot rolled spring steel C Si Mn P S Cr Al 0,67 0,22 0,75 <0,01 <0,01 0,23 0,03

Chemical composition: (typical analysis at Saarstahl in %) Deviation in chemical composition on request Application: Unalloyed steel for springs as belleville washers, spring plates and stabilizer bars for motor vehicles Hot forming and heat treatment: Forging or hot rolling: Normalizing: Soft annealing: Hardening: 1100 - 800°C 810 - 840°C/air 680 - 710°C/furnace 815 - 845°C/oil min. 59 HRC or 670 HV as quenched Mechanical properties: Condition of delivery Soft annealed (+A) or soft annealed and slightly rerolled (+LC) Quenched and tempered (+QT) 0,2% proof stress Rp0,2 [N/mm²] max. 510 1200 - 1900 Tensile strength Rm [N/mm²] max. 640 - Fracture elongation A80 [%] min. 16 - Hardness [HV] max. 200 370 - 580 Hardness [HRB] max. 92 - Hardness [HRC] - 38,5 - 54 Typical hardness values (HV) for quenched and tempered materials at different thickness ranges Effective thickness [mm] 0,30<=0,50 0,50<=0,75 0,75<=1,00 1,00<=1,50 1,50<=2,00 2,00<=3,00 Hardness [HV] 485 - 535 465 - 515 455 - 505 445 - 495 425 - 475 415 - 465

Additional Information:

• Item Code: 1188899
• Production Capacity: 1000 METRIC TONS
• Delivery Time: READY STOCK

Product Details:

We are the largest firm offering a huge quantity of C60 Steel Plates to vast customers’ base. Our products are highly appreciated for its perfect finish, optimum quality and sturdy nature. These mentioned items are much demanded across the market. To add to our advantage, we are delivering these items in a safe packaging material to avoid any defect during transportation.

 

Features:

• Precisely designed
• Optimum finish
• Reliable

C60 steel plate is one mainly of high carbon steel,EN 10083 C60 steel plate is one of the higher carbon content (0.60%) steels.It is more difficult to fabricate than the lower carbon grades.

C60 steel Chemical Composition

C60 steel Mechanical Properties

Additional Information:

• Item Code: C60
• Pay Mode Terms: L/C (Letter of Credit),T/T (Bank Transfer),D/P,D/A,Other

Product Details:

High Carbon Spring Steel combines ease of fabrication with good strength and surface finish, is valued for its strength properties and operates at significantly higher levels than the mild steel grades. High carbon steel strip can be finished to meet the needs of a wide range of products. Where tensile strength and hardness are required, High Carbon steels are the material of choice.


Grades :

• C60, C65, C70, C75, C85, HC-14, En 42 J, C-98, C-100, C-124 / HC21 etc.

 

We offer spring steel strip in various shapes and sizes according to your final uses.

These have excellent hardens property and high yield strength. Clients can avail these at competitive prices.
Nextgen Steel & Alloys is a large exporter of High Carbon Spring Steel in countries like Kuwait, Bahrain, Iraq, Oman, Qatar, Saudi Arabia and the United Arab Emirates (UAE), US, Singapore, Malaysia, Dubai, etc.

Product Details:

The springs use for counter balancing rolling shutter can be make from spring steel wire or flat spring steel strip. Flat spring steel strips are widely used in rolling shutter industies, due to its durability and 3000 cycles rolling up and down per year. It is usually cut into 3m, 3.5m, 5m, 5.5m, 6m from flat spring big coils. Flat spring steel trip used for garage door spring, the material shall be 0.65-0.75 percent carbon steel strip with hardened and tempered process. Blue tempered in flat spring steel strip, can be anti-corrossion for a long time without getting rust.


Grades :

• C60, C65, C70, C75, C85, HC-14, En 42 J, C-98, C-100, C-124 / HC21 etc.

Nextgen Steel & Alloys is a large exporter of C70 Spring Steel in countries like Kuwait, Bahrain, Iraq, Oman, Qatar, Saudi Arabia and the United Arab Emirates (UAE), US, Singapore, Malaysia, Dubai, etc.